Physical and mechanical properties of thermally modified wood from E. grandis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Decay resistance of thermally-modified Eucalyptus grandis wood at 140 degrees C, 160 degrees C, 180 degrees C, 200 degrees C and 220 degrees C

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Behavior of the brown-rot fungus Gloeophyllum trabeum on thermally-modified Eucalyptus grandis wood

In this study, we aimed evaluate the behavior of the brown-rot fungus Gloeophylum trabeum and white-rot fungus Pycnoporus sanguineus on thermally-modified Eucalyptus grandis wood. To this end, boards from five-year-eleven-month-old E. grandis trees, taken from the Duratex-SA company stock, were thermally-modified between 180 ºC and 220 ºC in the Laboratory of Wood Drying and Preservation at Universidade Estadual Paulista - UNESP, Botucatu, Sao Paulo state Brazil. Samples of each treatment were tested according to the ASTM D-2017 (2008) technical norm. The accelerated decay caused by the brown-rot fungus G. trabeum was compared with the decay caused by the white-rot fungus P. sanguineus, studied by Calonego et al. (2010). The results showed that (1) brown-rot fungus caused greater decay than white-rot fungus; and (2) the increase in temperature from 180 to 220 ºC caused reductions between 28.2% and 70.0% in the weight loss of E. grandis samples incubated with G. trabeum.

Removal of Zn(2+) from Electroplating Wastewater Using Modified Wood Sawdust and Sugarcane Bagasse

This paper describes the preparation of new adsorbents derived from sugarcane bagasse and wood sawdust (Manilkara sp.) to remove zinc (II) ions from electroplating wastewater. The first part deals with the chemical modification of sugarcane bagasse and wood sawdust, using succinic anhydride to introduce carboxylic acid functions into the material. The obtained materials (modified sugarcane bagasse MB2 and modified wood sawdust MS2) were then characterized by infrared spectroscopy (IR) and used in adsorption experiments. The adsorption experiments evaluates Zn(2+) removal from aqueous single metal solution and real electroplating wastewater on both batch and continuous experiments using fixed-bed columns prepared in laboratorial scale with the obtained adsorbents. Adsorption isotherms were then developed using Langmuir model and the Thomas kinetic model. The calculated Zn(2+) adsorption capacities were found to be 145 mg/g for MS2 and 125 mg/g for MB2 in single metal aqueous solution, whereas for the industrial wastewater these values were 61 mg/g for MS2 and 55 mg/g for MB2.

Effect of thermal modification on the physical properties of juvenile and mature woods of Eucalyptus grandis

This study aimed to evaluate the effect of thermal treatment on the physical properties of juvenile and mature woods of Eucalyptus grandis. Boards were taken from 30-year-old E. grandis trees. The boards were thermally modified at 180 °C in the Laboratory of Wood Drying and Preservation at UNESP, Botucatu, Sao Paulo state, Brazil. The results showed that thermal modification caused: (1) decrease of 6.8% in the density at 0% equilibrium moisture content of mature wood; (2) significant decreases of 14.7% and 35.6% in the maximum volumetric swellings of juvenile and mature woods, respectively; (3) significant decreases of 13.7% and 21.3% in the equilibrium moisture content of juvenile and mature woods, respectively. The influence of thermal modification in juvenile wood was lower than in mature wood and caused greater uniformity in the physical variations between these types of wood in E. grandis.

Variação dimensional de tábuas de Eucalyptus grandis durante alguns níveis de tempo e temperatura de termorretificação

The objective of this study was evaluate the effects of retification® temperatures and times on thickness variation from Eucalyptus grandis timber. Boards from logs of 30-year-old Eucalyptus grandis trees, from São Paulo Forest Institute in Santa Barbara, Brazil, were thermally modified at 180ºC for 2.5 hours, at 200ºC for 3.0 hours and 200ºC for 4.0 hours. The results showed that: (1) the thermally modified wood at 200°C by 3.0 to 4.0 hours showed increased thickness between 0.698 mm and 0.874 mm due to the internal cracks, (2) the thermally modified wood at 180°C by 2.5 hours has a decreased from 0,177 mm in thickness and the absences of internal cracks.

EFFECT OF THERMAL TREATMENT ON THE CHEMICAL CHARACTERISTICS OF WOOD FROM Eucalyptus grandis W. Hill ex Maiden UNDER DIFFERENT ATMOSPHERIC CONDITIONS

Thermal treatment (thermal rectification) is a process in which technological properties of wood are modified using thermal energy, the result of Which is often value-added wood. Thermally treated wood takes on similar color shades to tropical woods and offers considerable resistance to destructive microorganisms and climate action, in addition to having high dimensional stability and low hygroscopicity. Wood samples of Eucalyptus grandis were subjected to various thermal treatments, as performed in presence (140 degrees C; 160 degrees C; 180 degrees C) or in absence of oxygen (160 degrees C; 180 degrees C; 200 degrees C) inside a thermal treatment chamber, and then studied as to their chemical characteristics. Increasing the maximum treatment temperatures led to a reduction in the holocellulose content of samples as a result of the degradation and volatilization of hemicelluloses, also leading to an increase in the relative lignin content. Except for glucose, all monosaccharide levels were found to decrease in samples after the thermal treatment at a maximum temperature of 200 degrees C. The thermal treatment above 160 degrees C led to increased levels of total extractives in the wood samples, probably ascribed to the emergence of low molecular weight substances as a result of thermal degradation. Overall, it was not possible to clearly determine the effect of presence or absence of oxygen in the air during thermal treatment on the chemical characteristics of the relevant wood samples.

Effect of thermal treatment on the chemical characteristics of wood from Eucalyptus grandis W. Hill ex Maiden under different atmospheric conditions

Thermal treatment (thermal rectification) is a process in which technological properties of wood are modified using thermal energy, the result of which is often value-added wood. Thermally treated wood takes on similar color shades to tropical woods and offers considerable resistance to destructive microorganisms and climate action, in addition to having high dimensional stability and low hygroscopicity. Wood samples of Eucalyptus grandis were subjected to various thermal treatments, as performed in presence (140ºC; 160ºC; 180ºC) or in absence of oxygen (160ºC; 180ºC; 200ºC) inside a thermal treatment chamber, and then studied as to their chemical characteristics. Increasing the maximum treatment temperatures led to a reduction in the holocellulose content of samples as a result of the degradation and volatilization of hemicelluloses, also leading to an increase in the relative lignin content. Except for glucose, all monosaccharide levels were found to decrease in samples after the thermal treatment at a maximum temperature of 200ºC. The thermal treatment above 160ºC led to increased levels of total extractives in the wood samples, probably ascribed to the emergence of low molecular weight substances as a result of thermal degradation. Overall, it was not possible to clearly determine the effect of presence or absence of oxygen in the air during thermal treatment on the chemical characteristics of the relevant wood samples.

A study of the nanostructure of the cell wall of the tracheids of conifer xylem by x-ray scattering

The purpose of this study was to develop practical and reliable x-ray scattering methods to study the nanostructure of the wood cell wall and to use these methods to systematically study the nanostructure of Norway spruce and Scots pine grown in Finland and Sweden. Methods to determine the microfibril angle (MFA) distribution, the crystallinity of wood, and the average size of cellulose crystallites using wide-angle x-ray scattering were developed and these parameters were determined as a function of the number of the year ring. The mean MFA in Norway spruce decreases rapidly as a function of the number of the year ring and after the 7th year ring it varies between 6° and 10°. The mean MFA of Scots pine behaves the same way as the mean MFA of Norway spruce. The thickness of cellulose crystallites for Norway spruce and Scots pine appears to be constant as a function of the number of the year ring. The obtained mean values are 32 Å for Norway spruce and 31 Å for Scots pine. The length of the cellulose crystallites was also quite constant as a function of the year ring. The mean length of the crystallites for Norway spruce was 364 Å, while the standard deviation was 27 Å. The mass fraction of crystalline cellulose in wood is the crystallinity of wood and the intrinsic crystallinity of cellulose is the crystallinity of cellulose. The crystallinity of wood increases from the 2nd year ring to the 10th year ring from the pith and is constant after the 10th year ring. The crystallinity of cellulose obtained using nuclear magnetic resonance spectroscopy was 52% for both species. The crystallinity of wood and the crystallinity of cellulose behave the same way in Norway spruce and Scots pine. The methods were also applied to studies on thermally modified Scots pine wood grown in Finland. Wood is modified thermally by heating and steaming in order to improve its properties such as biological resistance and dimensional stability. Modification temperatures varied from 100 °C to 240 °C. The thermal modification increases the crystallinity of wood and the thickness of cellulose crystallites but does not influence the MFA distribution. When the modification temperature was 230 °C and time 4 h, the thickness of the cellulose crystallites increased from 31 Å to 34 Å.

Experimental Reinforcement of Wood Beams

Rehabilitation is becoming more and more usual in the construction sector in Portugal. The introduction of newer construction materials and technical know-how of integrating different materials for achieving desired engineering goals is an important step to the development of the sector. Wood industry is also getting more and more adapted to composite technologies with the introduction of the so called “highly engineered wood products” and with the use of modification treatments. This work is an attempt to explain the viability of using stainless steel and glass fibre reinforced polymer (GFRP) as reinforcements in wood beams. This thesis specifically focuses on the flexural behaviour of Portuguese Pine unmodified and modified wood beams. Two types of modification were used: 1,3-dimethylol-4,5- dihydroxyethyleneurea (DMDHEU) resin and amid wax. The behaviour of the material was analysed with a nonlinear model. The latter model simulates the behaviour of the reinforced wood beams under flexural loading. Small-scale beams (1:15) were experimented in flexural bending and the experimental results obtained were compared with the analytical model results. The experiments confirm the viability of the reinforcing schemes and the working procedures. Experimental results showed fair agreement with the nonlinear model. A strength increase between 15% and 80% was achieved. Stiffness increased by 40% to 50% in beams reinforced with steel but no significant increase was achieved with the glass fibre reinforcement.

Physical and chemical changes in juvenile and mature woods of Pinus elliottii var. elliottii by thermal modification

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of elevated atmospheric CO2 and O3 on wood density, antomical proerties and decomposition of Northern Hardwoods

Anthropogenic activities continue to drive atmospheric CO2 and O3 concentrations to levels higher than during the pre-industrial era. Accumulating evidence indicates that both elevated CO2 and elevated O3 could modify the quantity and biochemistry of woody plant biomass. Anatomical properties of woody plants are largely influenced by the activity of the cambium and the growth characteristics of wood cells, which are in turn influenced by a range of environmental factors. Hence, alterations in the concentrations of atmospheric CO2 and / or O3 could also impact wood anatomical properties. Many fungi derive their metabolic resources for growth from plant litter, including woody tissue, and therefore modifications in the quantity, biochemistry and anatomical properties of woody plants in response to elevated CO2 and / or O3 could impact the community of wood-decaying fungi and rates of wood decomposition. Consequently carbon and nutrient cycling and productivity of terrestrial ecosystem could also be impacted. Alterations in wood structure and biochemistry of woody plants could also impact wood density and subsequently impact wood quality. This dissertation examined the long term effects of elevated CO2 and / or O3 on wood anatomical properties, wood density, wood-decaying fungi and wood decomposition of northern hardwood tree species at the Aspen Free-Air CO2 and O3 Enrichment (Aspen FACE) project, near Rhinelander, WI, USA. Anatomical properties of wood varied significantly with species and aspen genotypes and radial position within the stem. Elevated CO2 did not have significant effects on wood anatomical properties in trembling aspen, paper birch or sugar maple, except for marginally increasing (P < 0.1) the number of vessels per square millimeter. Elevated O3 marginally or significantly altered vessel lumen diameter, cell wall area and vessel lumen area proportions depending on species and radial position. In line with the modifications in the anatomical properties, elevated CO2 and O3, alone, significantly modified wood density but effects were species and / or genotype specific. However, the effects of elevated CO2 and O3, alone, on wood anatomical properties and density were ameliorated when in combination. Wood species had a much greater impact on the wood-decaying fungal community and initial wood decomposition rate than did growth or decomposition of wood in elevated CO2 and / or O3. Polyporales, Agaricales, and Russulales were the dominant orders of fungi isolated. Based on the current results, future higher levels of CO2 and O3 may have moderate effects on wood quality of northern hardwoods, but for utilization purposes these may not be considered significant. However, wood-decaying fungal community composition and decomposition of northern hardwoods may be altered via shifts in species and / or genotype composition under future higher levels of CO2 and O3.

An investigation of effects of modification processes on physical properties and mechanism of drug release for sustaining drug release from modified rice

The aim of this study was to investigate the effect of modification processes on physical properties and explain the mechanism of sustained drug release from modified rice (MR). Various types of Vietnamese rice were introduced in the study as the matrices of sustained release dosage form. Rice was thermally modified in water for a determined temperature at different times with a simple process. Then tablets containing MR and isradipine, the model drug, were prepared to investigate the capability of sustained drug release. Scanning electron microscopy (SEM) was used to determine different morphologies between MR formulations. Flow property of MR was analyzed by Hausner ratio and Carr's indices. The dissolution rate and swelling/erosion behaviors of tablets were evaluated at pH 1.2 and pH6.8 at 37±0.5°C. The matrix tablet containing MR showed a sustained release as compared to the control. The SEM analyses and swelling/erosion studies indicated that the morphology as well as swelling/erosion rate of MR were modulated by modification time, drying method and incubation. It was found that the modification process was crucial because it could highly affect the granule morphologies and hence, leading to the change of flowability and swelling/erosion capacity for sustained release of drug.

Improvement of termite resistance, dimensional stability and mechanical properties of pine wood by paraffin impregnation

Paraffin has been used as surface protection of wood throughout the ages but its use for impregnation to improve wood resistance to biodegradation is recent. This study determined the main improvements on wood properties with paraffin impregnation. Healthy Pinus pinaster Ait. wood was impregnated with paraffin at different levels using a hot–cold process. Weight gain, equilibrium moisture content and dimensional stability (ASE) at 35 and 65 % relative humidity, termite durability against Reticulitermes grassei (Clément), bending strength, bending stiffness (MOE) and Janka hardness were determined. Density increased from 0.57 to 0.99, ASE ranged between 38–96 % and 16–71 % for 35 and 65 % relative humidity, respectively. Equilibrium moisture content decreased from 9.9 and 12.0 % to 0.8 and 3.6 % for 35 and 65 % relative humidity. Termite durability improved from level 4 to level 3 of attack, and higher termite mortality was found in treated wood (52 % against 17 %). Bending strength (MOR) increased with paraffin weight gain, reaching a 39 % increase. MOE also increased by about 13 % for wood with a weight gain around 80 %. Janka hardness increased significantly reaching about 40 % for wood with 80 % weight gain. Paraffin impregnated wood has improved properties with regard to equilibrium moisture content, dimensional stability and density, bending strength and Janka hardness, and resistance against termites.